Transfer label having ink containment layers, container comprising a transfer layer and method of washing such a container

ABSTRACT

The invention relates to a transfer label including a backing layer and a transfer layer which is releasably attached to the backing layer. The transfer layer includes an ink layer and on each side of the ink layer a top and bottom containment layer. The top and bottom containment layer contact one another outside the perimeter of the ink layer to form a closed envelop around the ink layer. The transfer label according to the present invention can be applied to a container such as a crate and can be easily removed therefrom in a washing process without the ink dissolving in the wash liquid.

This is a national phase application of International Application No. PCT/NL97/00137 filed on Mar. 19, 1997, now WO97/35290.

BACKGROUND OF THE INVENTION

The invention relates to a transfer label comprising a backing layer and a transfer layer which is releasably attached to the backing layer, the transfer layer comprising an ink layer.

The invention also relates to a container provided with a transfer layer according to the invention and to a method of removing the transfer layer from such a container.

It is known in the packaging technology art to label containers such as plastic crates by providing a non-removable permanent image by a silk screen method. Such labels offer a highly durable finish with two or three color availability. This technique however offers limited colors, lacks the improved graphics that other labelling techniques offer, is not flexible in its ability to have graphic changes to meet market strategies leading to large inventories of obsolete units, and tends to show signs of wear after about four trips.

When removable inks are to be applied to re-usable plastic crates by a screen printing or a tampon printing process, the inks have to be applied in the bottling plant, such as a brewery, which may lead to problems with respect to registration. Upon removal from the crates by means of crate washers, the inks will be dissolved in the washing liquid and in this way contaminate the crate washers. Furthermore the speed of application is limited, and curing of the inks requires a lot of space and long storage times prior to delivery.

A second way of labelling containers encompasses gluing printed paper labels to containers such as plastic crates or bottles at the time of filling and sealing. This type of labels however offer little resistance to label damage from handling and exposure to moisture (wrinkling). Furthermore, paper labels are difficult to remove from crates, and tend to clog the crate washers available today. Upon removal of paper labels from plastic crates, a glue residue may be left on the crates.

A third technique for labelling containers, in particular glass bottles is based on the principles described in WO 90/05088. In this publication, a method of labelling bottles is described which provides a durable, highly impact resistant label and yet permits high definition label printing. A transfer label comprising a removable backing layer is provided which backing layer is reverse printed with a vinyl or acrylic ink which is cured and overprinted with adhesive. The label is applied to the container with its adhesive surface in contact therewith. The backing layer is separated from the transfer layer of the label for instance by the application of heat to either the container, the label or to both. The labelled container is then applied with a coating which is subsequently cured. The cured coating provides the required degree of impact resistance and durability. The disadvantage of permanently attached labels, is that when these labels get scratched or otherwise damaged, they cannot be easily removed from the bottles. Also, it is not possible to provide the same containers each time with new and/or different labels, which is desirable for promotional activities.

It is an object of the present invention to provide a transfer layer which can easily be attached to a container and which can be removed in an environmentally friendly manner.

It is a further object of the invention to provide such a transfer label that can be removed in a wash process using a washing liquid, without the inks from the label contaminating the wash liquid.

It is a further object of the present invention to provide such a transfer label which has a good adherence during storage and use of the container, but which can very rapidly be removed from the container in an economic manner for replacing the label by a new and/or different labels.

It is another object of the present invention to provide such a label which utilizes water soluble inks as a printing substance, such inks being environmentally friendly and widely used in the food technology.

It is a still further object of the present invention to provide a returnable crate system which can be provided with attractive labels, that can be easily and economically be removed and re-applied. The labels should be applied and removed at relatively high speeds.

SUMMARY OF THE INVENTION

Thereto the transfer label according to the present invention is characterised in that the transfer layer comprises on each side of the ink layer a top and a bottom containment layer, respectively, the top and the bottom containment layer contacting one another outside the perimeter of the ink layer to form a closed envelope around think layer.

By entrapping the ink in the envelope between the containment layers, it is possible to remove the transfer layer from the container to which it has been attached, by a wet removal process such as a soaking process or a process utilizing high pressure water jets. The ink is prevented from leaking out of the envelope during such a process such that no contamination of the wash water occurs. During the wet removal process, not more than 10% by weight of the ink in a transfer layer is dissolved in an alkaline wash solution. Hereby it is prevented that the containers are discoloured by the inks. Furthermore, the ink levels in the wash solution remain low enough to not effect the aerobic and anaerobic treatment in the waste water treatment plants. The low concentrations of inks in the wash water prevent accumulation of metals in the sludge of the waste water treatment plants, such that this sludge will not have to be treated as chemical waste under government regulations. By simply collecting the removed labels from the wash liquid, a very economic wash process can be achieved.

Preferably the ink layer comprises separate zones of dimensions between 0.5 mm² and 500 cm², the top containment layer and the bottom containment layer contacting one another outside the separate zones to form individual envelopes around each zone of the ink layer. The areas of the transfer layer connecting the separate zones of the ink layer will have a reduced thickness compared to the zones where an ink layer is present between the containment layers. After transfer of the transfer layer to a container, it is possible that no label material is present outside the separate ink zones. These areas of reduced thickness or open areas of the labels outside the envelopes, form natural points of attack for the wash solution, such that the label can be removed in separate parts. Because the wash solution has access to the label-container interface via the areas outside the envelopes around the print patterns, a very rapid removal of the transfer layer from the container is possible whereby the label is removed in separate pieces. These pieces can be sieved from the wash solution using conventional sieves with openings having a size between 0.1 mm and 10 mm, preferably about 2 mm.

Although it is preferred to use the transfer layer according to the present invention on re-usable plastic crates, the label can also be used in combination with plastic bottles, such as PET-bottles, plastic food trays, glass bottles and the like.

A preferred transfer label according to the present invention comprises a transfer layer which is permeable for the soaking liquids.

With “permeable” it is meant that a transfer layer has water, uptake value after 3 hours between 0.0 and 100 g/m², preferably about 5 g/m², in water at room temperature. Such labels have a water vapour transmission rate between 50 and 750 g/m², preferably about 600 g/m² after 24 hours for water at room temperature. The transfer layer may comprise a cover layer overlaying the ink pattern, which cover layer forms the outwardly facing surface upon attachment of the transfer layer to a container. The cover layer may for instance be formed by an acrylic wax coating. The cover layer may be a continuous layer, or may be discontinuous and printed in register with the ink pattern. The acrylic wax cover layer can very advantageously be penetrated by for instance a 0.5% NaOH-solution, while providing a sufficient barrier to penetration of moisture during storage and use-conditions of the label on a container. Labels according to the present invention which combine sufficient durability with quick and economic removal have a pencil hardness between 1N and 7N in the dry state and a pencil hardness less than 0.5 N after a soaking time between 1 minute and 15 minutes in water at 20° C.

Preferably the transfer layer has such a configuration that it breaks up in at least four pieces under turbulent soaking conditions in an aqueous liquid of a temperature below 100° C. preferably below 70° C. within a soaking time of not more than 20 minutes preferably not more than 10 seconds. As the transfer layer is detached from the container, the size of the majority of the pieces formed upon breaking up of the transfer layer preferably is not smaller than the dimensions of the separate zones of the ink pattern. Although some of the envelopes may rupture during the wash process, this causes relatively little leakage of the ink contained within the envelopes as these inks will still be surrounded by a substantial part of the containment layers.

By use of the containment layers according to the present invention, water soluble inks may be used. In a preferred embodiment the topmost containment layer comprises an unpigmented ink which is compatible with the underlying printed zone. The bottom containment layer preferably comprises an adhesive layer or an intermediate layer which is compatible with an underlying adhesive layer and with the above located ink zone layer.

The top containment layer may be discontinuous and printed in register with the ink pattern. In this way the bottom containment layer may be directly attacked by the wash liquid during removal of the transfer layer. When the bottom containment layer is also discontinuous, the underlying adhesive layer can be directly attacked by the wash liquid. In a preferred embodiment both containment layers and an underlying adhesive layer are discontinuous and all printed in register.

After application of the transfer layer to the container, a cover layer may be applied across the transfer layer the cover layer comprising an acrylic wax. The acrylic wax is relatively impervious to water such that a good resistance of the label against scratching and removal of the label during use of the container is provided. The acrylic wax cover layer however is pervious to an aqueous alkaline solution such that the transfer layer can easily be removed by for instance a 0.5% NaOH-solution.

Preferably the transfer layer is heat-treated after having been applied to a container to cause a shrinking of at least parts of the transfer layer. By the heat treatment, a coalescing of the different layers of the transfer label takes place.

A label according to the present invention that combines sufficient durability during storage and use with quick and economic removal has preferably been heat treated after application to the container at a temperature between 40° C. and 100° C., more preferably between 50° C. and 90° C.

By carefully selecting the composition of the label, the use of a protective coating and the nature of the post treatment (heat treatment) it is possible to steer the properties of the transfer layer, especially with respect to the behaviour during washing.

The selection of the adhesive to be used in adhering the label image to the container surface will influence the wash-off properties. The adhesive must have been activated prior to or during application of the transfer layer to the container. An easy and generally preferred method of applying the image is through the use of heat activatable adhesives that have been applied to the image in the form of a reverse printed label. Other methods include the use of adhesive that can be activated through radiation, chemicals, electron-beam, micro-wave, UV and the like. It is also possible to use adhesives that can be activated through photo initiation, humidity, enzymatic action, pressure or ultra-sonic treatment.

A preferred adhesive has a low tack temperature, preferably between 60° and 90°, more preferably between 80° and 90°. Instead of a separate layer of adhesive it is also possible to use in the transfer layer an ink which in itself has adhesive properties upon activation.

Preferably the application surface of the container for receiving the transfer layer has a surface tension of at least 60 Dyne per cm. The method of washing a container comprising a transfer layer according to the present invention comprises the steps of:

placing the container in a soaking solution during a soaking time not longer than 20 min, preferably not longer than 1 minute, the temperature of the soaking solution being below 100° C., preferably below 70° C., while causing turbulence in the soaking solution such that the label breaks up in at least 4 parts, each part not smaller than 5 micrometers and is detached from the container, the majority of the ink remaining contained inside the envelopes,

pumping the soaking solution through a sieve and collection of the pieces of the label on the sieve,

periodically cleaning the sieve by collection and removal of the label pieces.

A transfer layer according to the present invention can be removed using conventional crate-washing equipment wherein the detached label pieces can be removed from the soaking solution by means of sieving. As no parts of the label dissolve in the soaking solution, no specific treatment equipment needs to be employed for cleaning the wash solution.

BRIEF DESCRIPTION OF THE DRAWINGS

Embodiments of a transfer label and a washing method according to the invention will be described hereafter in detail with reference to the accompanying drawings. In the drawings:

FIG. 1 shows a heat transfer label according to the invention wherein separate ink patterns are each contained in an individual envelope,

FIG. 2 shows a washing device for removal of a transfer layer according to the present invention from a container, in particular from a plastic create.

FIG. 3 shows a cross-sectional view of the washing device according to FIG. 2 along the line III—III.

FIG. 4-7 show various embodiments of the transfer layer of a transfer label according to the present invention,

FIG. 8 schematically shows a plan view of an embodiment of a transfer label according to the invention comprising differently sized envelopes around the ink pattern,

FIG. 9 schematically shows a method of applying the transfer layer according to the present invention, to a returnable crate, and

FIGS. 10 and 11 graphically show the removal time of a transfer layer at different post heat temperatures without a wax cover layer and with a wax cover layer respectively.

DETAILED DESCRIPTION OF THE INVENTION

FIG. 1 shows an embodiment of a transfer label 1 according to the present invention comprising a carrier, or backing layer 2 formed by for instance a two-mil thickness polypropylene film. A silicone layer 3 is located on the carrier, or backing layer 2. On the silicone layer 3 a transfer layer 4 is placed which consists of a top containment layer 5,5′ an ink layer 7, 7′, a bottom containment layer 6,6′ and an adhesive layer 8, 8′.

Upon attachment of the transfer layer 4 to a container, the carrier layer 2 and the silicone layer 3 are removed under application of heat and pressure. The adhesive layer 8 bonds the transfer layer 4 to an underlying container surface, and the outwardly facing layer is formed by the top containment layer 5, 5′.

The label carrier 2 which is provided with the electron beam cured silicon layer 3 can be for instance a polypropylene film of 1 to 3 mils thickness as supplied by Mobil Chemical, Films Division, Rochester, N.Y. Prior to printing of the top containment layer 5, 5′ onto the silicone layer 3, the silicone surface must be corona treated. A corona treatment will allow uniform wetting of the print materials and still allow for release of the transfer layer 4. Preferably the corona treatment is applied to the carrier layer 2 and silicone layer 3 shortly before the first print of the top containment layer 5 is applied. A target treatment level should be approximately 30% of 3,5 kW.

During handling of the silicone-coated carrier layer 2, care is taken not to scratch the silicone layer 3. Scratching the silicone layer 3 would allow the top containment layer 5 to contact and adhere to the underlying polypropylene film 2 which would adversely effect the transfer of the transfer layer 4 during application.

The top containment layer 5, 5′ consists for instance of unpigmented ink and has several functions. Firstly, it slows or prevents water penetration into the underlying ink layer 7,7′. As the layer 5, 5′ is printed wider than the underlying ink pattern 7,7′ it forms part of an envelope which totally surrounds the colored ink layers 7,7′. Furthermore, the top containment layer 5, 5′ provides a consistent medium between the inks and the silicone release surface 3. The layer 5, 5′ is very important to the overall transferability of the label and should be applied at a weight of at least 1.4 g/m². It is important that upon application of the top containment layer 5, 5′ this layer is free of airbubbles and pinholes. Furthermore, the top containment layer must be dry before printing the subsequent ink layer 7,7′ thereon.

After printing the top containment layer 5,5′ onto the release layer 3, an optimum peel force of 100 g or less should be measured in a standard tape peel test. Within five hours after application, the peel force of the top containment layer will be about 60% less, or 40 g. With the specified peel force, the containment layer 5 should be removed completely. A suitable material for the top containment layer 51 is available from Environmental Inks and Coatings, Morganton, N.C. under type number 1304.

Examples of a preferred ink for the ink layer 7,7′ include a waterborne organic as available from Environmental Inks and Coatings, Morganton, N.C. under type number Aqua BW EH-31721, EH 52016, EH 90967. Theses inks have a high stability even at temperature over 200° C. without discoloration or loss of adhesion.

The bottom containment layer 6,6′ provides a strong interface between the adhesive layer 8,8′ and the colored ink layers 7, 7′. It is formulated to chemically anchor to the ink and provide excellent wetting and bounding of the adhesive layer. The bottom containment layer 6,6′ attaches outside the ink layer 7,7′ to the top containment layer 5,5′ such that a closed envelope is formed around the separate ink patterns 7, 7′. A suitable material for the bottom containment layer 6,6′ is available from Environmental Inks and Coatings, under type no. XP 11358.

The adhesive layer 8,8′ can be formed by a waterborne organic material which is printed in a number of consecutive flexographic stations such as three stations, or can be floodcoated on a single station. The adhesive layer 8,8′ may also be applied by a single gravure printing station. Preferably the adhesive 8,8′ is heat-activated and has a low tack temperature from 80° C. up to 107° C. The preferred weight of adhesive is approximately, 3.5 g/m².

The layers of the transfer layer 4 may be applied in a flexographic printing press with up to 10 printing stations. Five stations may be used for printing the layers 5,5′, 6,6′ and the adhesive layer 8,8′ which can be composed of three separate adhesive layers. Five types of colored ink 7,7′ may be applied using the five remaining flexographic printing stations.

Instead of a flexographic printing process, also a gravure press equipped with a corona treater may be used. Because material laydown is heavier than in the flexographic process, only three gravure printing stations may be necessary for applying the containment layers 5, 5′ and 6, 6′ and the adhesive layer 8, 8′.

Further, rotary screen printing processes can be used for applying layers 5,5′, 6,6′ and 8,8′. Upon printing of the bottom containment layer 6,6′, care should be taken that it extends beyond the perimeter of the ink patterns 7, 7′ but remains within the perimeter of the top containment layer 5,5′. It is preferable that the adhesive layer 8,8′ extends beyond the perimeter of the bottom containment layer and matches the perimeter of the topmost containment layer 5,5′.

FIG. 2 shows a schematic side view of a crate washing apparatus for removing the transfer layers according to the present invention from crates 12 that are supplied to the crate washer 10 via a transport conveyor 11. Crates 12 are first transported to pre-rinsing station 13 and sprayed with a pre-rinsing solution which is applied from a number of nozzles 14 located above and below the transport conveyor 11. The speed of the conveyor 11 is such that the dwell time of the crate 12 in the pre-rinsing station is between 6 and 8 seconds. The temperature of the pre-rinse solution is 60° C. The pre-rinse solution preferably comprises a 0.5% NaOH solution.

After passing through the pre-rinsing station 13, the crates are transported through a soaking station 15 via a downwardly sloping section 16 of the conveyor 11. The dwell time of crate in the soaking station is between 10 and 40 seconds. In the soaking station, the crate is completely submerged and a soaking solution is recirculated in the soaking station 15 by means of nozzles 35 to cause turbulent soaking conditions. The turbulent soaking conditions may for instance include recirculating the liquid from the soaking station 15 via the nozzles 35 at a rate of 60 m³/h for a total volume of the soaking solution of 5 m³. It is important that the transfer layers are completely removed from the crates 12 in the soaking station 15, without any pieces remaining on the crates. Such remaining pieces would, when dried, adhere firmly to the crates and form an undesired contamination of the crate surface.

From the soaking station 15, the crates are transported via the upwardly sloping conveyor track 17 to an after-rinse station 18. The after-rinse solution may comprise water at a temperature of 30° C. The dwell time of the crates in the after-rinse station 18 is between 6 and 13 seconds.

Connected to each rinsing station 13, 18 and to the soaking station 15 are sieving sections 20, 21 and 22. Each sieving section comprises a rotating belt sieve 23, 24, 25, which are driven by motors 26, 27, 28 respectively. Pumps 29, 30 and 31 draw the rinsing liquid and the soaking liquid from each perspective station through the rotating sieve belts 23, 24, 25 a rate of for instance 60 m³/h. The sieved liquids are recirculated back to nozzles 14 and 19 in the pre-rinse and after-rinse stations 13, 18 respectively and to the soaking station 15.

FIG. 3 shows a cross-sectional view along the lines III—III of FIG. 2. It can be seen that the sieve belt 24 is rotated around two rollers 37, 38. The top end of the sieve belt 24 extends above the level of the soaking liquid in the soaking station 15. The sieve belt 24 comprises a dual layer belt-like sieving element with a mesh size of 2 millimetres. During operation it is important to continuously rotate the sieve belt 24 to prevent the label pieces from the transfer layers that break up into pieces in the soaking station 15, from clogging the sieve belt. A spraying nozzle 39 cleans the surface of the belt-like sieving elements by high pressure water or air jets. The removed label elements are collected in a collection compartment 40.

It was found that a very efficient removal of labels from crates 12 is achieved by using 0.5% NaOH-solution in the pre-rinsing station 13 and the soaking station 15. However, it is also possible to apply a pre-treatment material onto the labels, prior to entry into the crate washer 10, which acts to soften the label prior to entry into the crate washer. For instance, a surface active component can be sprayed onto the crates 12 when travelling to the crate washer 10. It is also possible to apply a gel-like material of a chemical composition which starts attacking the label prior to entry into the crate washer 10. In such a case it may be possible to use water only in the crate washer 10, instead of the alkaline solution.

FIG. 4 shows an alternative embodiment of a transfer label according to the invention comprising a backing layer 48, a silicone release layer 49 and a transfer layer 50. The ink layer 52 of the transfer layer 50 is a continuous layer which may for instance have dimensions of 10 by 10 centimeters. The top containment layer 51 and the bottom containment layer 53 encase the ink layer 52 and engage one another around the perimeter of the ink layer. Hereby a single envelope is formed around the ink layer 52. During removal of the transfer layer 50 from a container to which it has been applied, the transfer layer 50 may rupture into several pieces. Thereby the envelope formed by the top and bottom containment layers 51, 53 will be ruptured. However it was found that still sufficient containment in that case occurs to prevent the ink layer 52 from dissolving in the wash solution.

In the embodiment of FIG. 5, the ink layer 52 is formed of separate zones 52,52′. Each zone of the ink layer may be formed by for instance individual letters, individual sentences, or individual blocks of words. The individual zones 52,52′ can also be formed by other graphic objects. It is shown that the top containment layer 51 attaches to the bottom containment layer 53 around the perimeter of each individual ink zone 52,52′. Thereby envelopes around each individual ink zone are formed and efficient containment is possible.

In the embodiment of FIG. 6, the top containment layer 51 is formed of separate zones 51,51′. Through the open areas between the separate zones of the top containment layer 51,51′ the wash solution can easily penetrate and attack the underlaying containment layers 53 and adhesive layer 54.

As shown in FIG. 7, the adhesive layer 54, the bottom containment layer 53, the ink layer 52 and the top containment layer 51 are each printed in register and form separate zones 51, 51′, 52, 52′, 53, 53′ and 54, 54′. Such a transfer layer has a very attractive appearance and the container surface is clearly visible in between each individual ink zone 52, 52′. With this specific construction, a very rapid washability is achieved as the wash liquid can very rapidly attack the adhesive layer 54, 54′ by penetrating through the open areas between each ink zone 52, 52′.

As shown in FIG. 8, a transfer layer according to the present invention can be comprised of several parts. For instance a graphic object 55 such as a picture can consist of a single ink layer which around its perimeter 55′ is encased between an upper and a lower containment layer, of a structure as shown in FIG. 4. Instead of the graphic object 55, separate lines of text 56 may be encased between an upper and a lower containment layer, for instance with a structure according to FIG. 5, FIG. 6 or FIG. 7. As indicated at 58, individual letters in a sentence may be each be individually encased between the top and bottom containment layer.

FIG. 9 shows a schematic view of the application process of a transfer layer from a transfer label according to the invention to a returnable, crate 59.

The label application process will now be described in the order of progression. Station 60 shows the step of surface treatment and temperature stabilization by means of a pre-heating treatment using a flame heater or burner 60′. For adhesion of two polymeric materials to occur, many factors must be considered such as cleanliness, pressure, temperature, contact time, surface roughness, movement during bonding and adhesive film thickness. An additional important consideration is the critical surface tension. The commonly accepted method of measuring the critical surface tension is with a Dyne solution, which is well known. For most adhesive applications the critical surface tension of polyethylene is 31 Dynes per centimeter. A series of tests were performed which demonstrated for best adhesion of the adhesive previously described to the polyethylene surface, a treatment level of 60 to 70 Dynes per centimeter was necessary. Further testing of commercially available equipment showed that flame treatment optimized both capital cost, operating cost and time required to achieve the required critical surface treatment.

For the adhesive to achieve and maintain tack quickly it is necessary to heat the polyethylene crate 59 at station 61 before the label adhesive is in contact with it. To avoid deforming of the container, it is desirable not to heat the surface over 20° F. (93° C.). As the surface temperature leaving the flame treatment is approximately 125° F. (52° C.), it is necessary to heat the surface approximately 75° F. (24° C.) at station 61. Here again, many options are available for heating. Hot air, additional flame heaters, gas fired infra-red panels and electric ceramic panels were all tested and found to be either too slow or difficult to control. It was found that an electrically heated flat fused quartz emitter plate 61′ with zonal band control for localized label transfer would provide maximum free air transmission of infra-red energy without the effects of ambient environmental factors. With an emissivity of 0.9 for polyethylene a desired emitter plate temperature of between 1652° F. (900° C.) to 1725° F. (940° C.) will emit the most efficient wavelength (2.5 to 3.2 μm) of infra-red energy for peak absorption. The unit tested was rated at 60 watts per square inch. The time to heat the polyethylene surface the necessary 75° F. (24° C.) was 4.5 seconds at a distance from the emitter plate of 2.5 centimeters.

Station 62 illustrates the method of label application whereby the printed ink materials are transferred from the polypropylene film substrate to the polyethylene surface utilizing the tactile characteristics of the heat activated adhesive to overcome the bond of the transfer layer to the corona treated silicone coating. The factors that influence transfer are time to contact, temperature and pressure applied during contact and film tension during contact particularly tension of the film after ink release. The diameter of pressure roll 63 is also a factor but not a variable. For this application the roll diameter is 38 mm. The roller 63 is made of silicone rubber over a steel core, with rubber durometer ranging from 50 Shore A to 80 Shore A. It should be noted that distortion (flattening) of the rubber roller is less at higher durometer, consequently the contact area is less and the transfer pressure is greater. This is important at the higher line speeds where contact time is minimized. Thus a crate moving 18.3 meters per minute (60 feet per minute) past a roller of 38 mm diameter will have a contact time of 1 millisecond per 1 degree of roller rotation where there is no roller distortion.

Roller pressure is provided by an air cylinder 64 activated by a conventional solenoid valve which in turn is operated by two (2) proximity switches, one to advance the roller and the other to retract. Other means, such as mechanical linkage are obvious and will not be listed here. The pressure is distributed across the length of the cylinder and for this particular label, transfer ranges from 12 to 17 kilograms per centimeter of roller length are desirable.

Thus the invention results in the film being advanced at exactly the same rate as the crate is moving past the roller by virtue of the heat activated adhesive adhering to the high energy crate surface. The pressure roller 63, which rotates freely, maintains the same tangential speed as the linear speed of the film and crate. Thus the ink is transferred completely and without distortion.

For purposes of fast and complete adhesion the pressure roller 63 is molded to a hollow core. Suspended within the hollow core is a resistance heater operated through a controller. The heating element, rated at 500 W, will maintain the roller surface at any predetermined temperature. For purposes of the invention, the roller surface temperature range between 250° F. and 370° F. (120° C. and 190° C.).

Many silicone coated polymer films may be used for the printed substrate. High temperature films such as polyester may be operated in continuous contact with the heated roller. Low temperature films such as polypropylene must be prevented from contacting the heated roller during pauses in the labelling operation. To accomplish this, film guides 65 are used to support the film when the roller is retracted. The guides 65 are mounted to maintain a clearance of approximately 13 mm between the guides and the labelled surface. At the same time the roller is retracted approximately 13 mm behind the film. By maintaining those clearances, stretching and distortion of the film such as polypropylene is avoided. High temperature films would not require the guides.

It has also been discovered that film tension, especially on the film exit side of the roller, is important to complete ink transfer. Through trials, it was found a continuous tension of approximately 2.5 kilograms is useful. This is achieved through a spring loaded dancer arm and roller.

Conventional nip rollers and stepping motors are used to advance the film to the next label and position it accurately, using a printed mark to trigger an optical scanning device.

Protection of the ink against scratching by casual handling as well as insuring its weatherability when subjected to outdoor storage is achieved with the application of an acrylic based wax water emulsion at station 66. This is applied by a roll applicator 68 which is supplied from a wet roller with a controlled amount of coating. Control is achieved with a doctor blade. The coating extends well past the edges of the ink pattern and seals the edges from intrusive moisture.

The final processing step is to coalesce the layers of the coating, label ink, and adhesive at station 67 by means of flame heater 67′ and also to inter diffuse the adhesive layer with the polyethylene substrate formed by the crate 59. This discovery was made through extensive trials of many heating systems. As flame treatment was discovered to be the best technique that would provide the required surface energy for label adhesion, so it was discovered that flame treatment of the label and coating composite was the best technique that would develop the required water immersion durability without sacrificing mechanical properties or altering the visual characteristics of the applied label, or distorting the polypropylene crate 59.

To illustrate the various properties which influence the adherence and the washability of the preferred transfer layer according to the present invention, the following tests were carried out, including a washing trial, a pencil scratch test, a water uptake/release test and a water vapour transmission rate test as described hereafter.

Washing Trial

To determine the optimum washing conditions for the labels according to the present invention, a transfer layer 50 having the configuration as shown in FIG. 4 was applied to a polyethylene crate. The dimensions of the label were about 10 by 10 centimeter and the adhesive layer 54 was a 100% urethane adhesive with a tack temperature of 79° C. The labels were applied to the crate with a temperature of roller 63 in FIG. 9 of 155° C. at a roller pressure of 2.5 bar. The pre-heat temperature of the crate (in stations 60 and 61 of FIG. 9), was 75° C. The speed of the crates 59 through the label applicator was 40 crates per minute. To determine the influence of the post-treat temperature with which the crates after label application were heated in station 67 of FIG. 9, post-treat temperatures of 40° C., 65° C. and 90° C. were used. After label application the crates were stored for at least 24 hours at a temperature of 20° C. The crates to which a label was applied, were thereafter soaked in a 0.5% NaOH-solution at temperatures of 20° C., 50° C. and 70° C.

The soaking of the crates was carried out in a soaking bath of 20 liters without turbulence, for such a soaking time (10-50 seconds) that after spraying the soaked crate with a showerhead at a rate of 6 liters/minutes, the label was completely removed within 2 seconds.

A second set of crates was prepared wherein after label application, a coating layer of wax was applied, such as at station 66 of FIG. 9.

The results of the soaking times required for label removal within 2 seconds, versus the post-treatment temperature, are given in tables I and II. From table I, the results of which are displayed graphically in FIG. 10, it can be seen that for labels to which no wax layer was applied the soaking time decreases drastically at temperatures of the soaking solution above 20° C. For post-heat temperatures of 90°, the durability of the label was increased and the soaking times remain above 5 seconds.

TABLE I crate washing trial (no wax layer applied) 0.5% caustic T postheat Time Time Time Average (° C.) (° C.) (sec) (sec) (sec) (sec) 20 none 90 120 105 40 180 150 165 65 210 240 225 90 480 420 450 50 none 2 2 2 2 40 3 3 3 3 65 3 3 4 3.3 90 15 14 13 14 70 none 1 1 1 1 40 1 1 1 1 65 1 1 1 1 90 5 6 7 6.3

It was found that an optimum post-heat temperature was between 65° C. and 90° C. At a post-heat temperatures below 65° C., too little coalescing of the applied transfer layer was achieved, such that the applied transfer layers had insufficient durability and could be too easily removed during storage and use. At post-heat temperatures higher than 90° C., the durability of the transfer layer became too large, and quick removal times could not be achieved in an economically feasible manner. During the spraying period with the showerhead, it was observed that after soaking, the labels detached from the crate and broke up in several (2 to 4) pieces.

When prior to the flame treatment step at station 67 in FIG. 9 a wax layer is applied at station 66, the durability of the labels is improved, and soaking times are increased. From table II it can be seen that for a 0.5% caustic solution, the wax coating leads to longer soaking times. The results of table II are displayed in graphical form in FIG. 11.

TABLE II crate washing trial (with wax layer applied) 0.5% caustic T postheat Time Time Time Average (° C.) (° C.) (sec) (sec) (sec) (sec) 20 none 150 150 150 40 180 180 180 65 300 270 285 90 <600 600 50 none 4 4 5 4.3 40 6 6 6 6 65 7 7 8 7.3 90 13 14 16 14.3 70 none 2 2 3 2.3 40 2 2 2 2 65 2 2 2 2 90 6 6 7 6.3

It was observed that by trying to remove the labels as were tested in the washing trial described above, solely with high pressure water jets at 20° C. and at a pressure of 120 bar, at a conveyor speed of 15 meters per minutes and a spraying angle of 90° at a distance of 10 centimeters, on label removal was achieved. Even for labels without any wax coating and no post-heat treatment, no removal by means of high-pressure water jets was possible.

Pencil Scratch Test

The purpose of the pencil scratch test is to identify the minimum and maximum durability of a label which can be obtained by taking different measures such as the use of a covering wax layer and heat treatment to cause coalescing of the label layers. Crates with labels which were applied with different post-heating temperatures, with and without wax, have been tested.

The labels were the same labels as used in the washing trial described above, and were applied to the crates under the same conditions.

The pencil scratch tests were carried out with a “scare resistance test model 435” supplied by Erichsen (PO Box 720, D-5870 Hemer Germany).

During the scratch test, a pencil with a plastic insert was used to scratch the label at an angle of 90° horizontally in the middle thereof.

After label application, the crates were stored for at least 24 hours at a temperature of 20° C. Prior to scratching, the crates were soaked in a water without turbulence at 20° C. The results of the scratch test are given in table III and table IV in which the scratch results are given in N.

TABLE III Pencil scratch test (in N) label without wax coating Post-heat Temperature soaking time (min) (° C.) 0 0.5 1 1.5 2 2.5 3 3.5 none 1 0.4 0.2 0.1 1 0.3 0.2 0.1 40 1.3 0.9 0.2 0.1 1.1 0.7 0.2 0.1 65 1.1 0.7 0.2 0.1 1 0.5 0.1 0.1 90 1.5 1.2 0.8 0.6 0.6 0.4 0.2 0.1 1.1 1 0.8 0.6 0.5 0.3 0.2 0.1

TABLE IV Pencil scratch test (in N) label with wax coating Posttreat soaking time (min) (° C.) 0 0.5 1 1.5 2 2.5 3 4 5 6 7 8 9 10 none 5 3 1.4 0.5 0.3 0.2 0.1 5 3 1.5 0.7 0.4 0.2 0.1 40 5 2.8 1.3 0.4 0.3 0.1 5 3 1.4 0.6 0.4 0.2 0.1 65 5 2.5 1.2 0.5 0.3 0.2 0.1 5 2.9 1.3 0.5 0.2 0.1 90 5 4 2.5 1.3 0.7 0.7 0.6 0.4 0.4 0.4 0.3 0.3 0.3 0.3 5 1 2.8 1.5 0.8 0.7 0.5 0.3 0.3 0.3 0.2 0.2 0.2 0.2

From table III and IV it can be seen that the post-heat flame treatment does not seem to influence the scratch resistance of the transfer layers significantly in the dry state. The durability of the transfer layer however is increased by the post-heat flame treatment, as is apparent from the higher pencil hardness after soaking. From table IV it appears that application of a wax layer covering the label, improves the scratch resistance of the dry label significantly. It was found that for high post-heat flame treatment temperatures of 110° C. in combination with a wax coating, a scratch force of 8 Newton was achieved. Labels with a pencil hardness of 8 Newton are considered to be semi-permanent labels which cannot be removed in an economically feasible manner.

Also at post-heat temperatures above 90° C., problems occurred during labelling as at these temperatures the polyethylene crates became brittle after a few applications, the crate pigments were found to discolorate and deformations of the softened crates on the conveyor and the pelletizer were found to occur.

At a post-heat temperature below 65° C., the strength of the labels was found to be insufficient for labels which did not have a wax coating. For labels without a wax coating the target pencil hardness in the dry state should be around 1.2 N and the soaking time until the scratch force drops below 0.3 Newton should be below 3 minutes. For a wax coated label, the target scratch force should be about 5 Newton in the dry state and the soaking time until the scratch force drops below 0.3 N should be below 10 minutes. Transfer layers having the above properties were found to have an optimal combination of durability and washability.

Water Uptake Test

The labels according to the present invention can be easily removed from a container, in particular from a plastic crate due to their specific water permeability which allows the soaking solution to penetrate the label, and subsequently break up the label in pieces and detach it from the container. It was found that preferred labels have a water absorption of around 5 g/m² after 3 hours in a water uptake test as described below. Labels according to the invention have a water uptake value higher than 0 and less than 100 g/m² in 3 hours. The water release of a preferred label was 4.5 g/m² within 30 minutes in the water release test as described below. Preferred labels according to the present invention will have a water release value greater than 0 (a complete barrier) and less than 100 g/m² after 3 hours.

Two samples were prepared, each sample containing 2 labels of a thickness of 12.7 microns each at 22.4° C. and 48% relative humidity, each sample having a surface area of 85.8 cm². For each sample, two labels were applied on a single piece of clear glass of 3 inch×9 inch×0.02 inch. Due to the extremely low weight of the labels it was necessary to apply two labels per piece of glass to obtain a weight that would register within the range of a two decimal place electronic gram scale.

The samples were prepared as follows: the glass supports were thoroughly cleaned and placed in a heating oven until an approximate temperature of 250° F. was reached on the glass surface. The glass was then removed from the heating oven and placed on a silicone rubber mat. A label was immediately set on the glass and secured to the surface by the use of a silicone roller. Rolling pressure was continually applied to the full length of the label until all entrapped air was removed (approximately 5-6 back and forth motions). After the glass had cooled, the carrier film was removed. Thereafter the opposite side of the glass plates were labelled by heating a clean aluminium plate (slightly larger than the glass plate) to approximately 250° F. in a convective oven, then placing the glass on the surface of the aluminium plate (label surface down) which allowed the heating of the glass upper surface. The label was then applied and secured in place by the silicone roller as described above. Once again, when the glass cooled, the carrier film was removed. Next a wax coating having a dry weight of 0.043 grams was applied to the surface of both labels. In the final step, using a propane oxidizing flame, flame treatment was applied to both labels by quickly passing the flame across the entire surface of the label sample. Once the samples were cooled the labels were ready for the Water Uptake test.

A stainless steel immersion tank of a 33.66 centimeter diameter and 24.13 centimeter height was filled with the deionized water, Care was taken that the water level was deep enough to allow total immersion of the sample. The sample was placed with the short dimension set perpendicular to the bottom of the tank. The glass supports were placed on a thin wire frame in the immersion tank. A thermocouple was installed inside the water immersion tank. After each time period, as given in table V, the sample was removed from the tank, excess surface water was blotted dry, the sample was weighted and placed back in the tank. This procedure was continued for the duration of the test. The results are shown in table V. With regard to sample 1, this sample reached it maximum absorption of 0.04 grams at the 3 hour mark and maintained this level to the 5 hour mark before giving up its ability to retain water at this level. After the 5 hour period the label lost its ability to hold water. We believe this phenomenon was caused because of label structure degradation. For sample 2, this sample also reached its maximum absorption of 0.04 grams at a 3 hour mark. At the 5 hour mark this sample was terminated from further testing in preparation for the water release test described below.

From the water uptake test, it can be deduced that a preferred label of a thickness of 12.7 microns has a water uptake value of 0.04g/85.8 cm² or about 5g/m² after 3 hours at room temperature.

TABLE V Water Uptake Test Room Air Sample 1 Sample 2 Relative Tank Water Tempe- Weight in Weight in Humidity Tempera- rature Time grams grams (%) ture (° F.) (° F.) 8:00 a.m. 59.77 59.77 47 71 72.4 8:10 a.m. 59.80 59.80 47 71 72.4 9:00 a.m. 59.81 59.81 47 71 72.4 10:00 a.m.  59.83 59.83 47 71 72.4 11:00 a.m.  59.85 59.85 48 72 72.4 12:00 p.m.  59.85 59.85 48 72 72.6 1:00 p.m. 59.85 48 72 72.6 2:00 p.m. 59.84 48 72 72.6 3:00 p.m. 59.81 49 72 72.6

In order to calculate individual label gram weights from the data in table V, refer to the following:

Each sample incorporated the use of two labels. To calculate the weight of Sample 1 at 1:00 p.m., substract the 8:00 a.m. reading from the 1:00 p.m. reading and divide by 2

As an example:

1.00 p.m. reading 59.85 8.00 a.m. reading 59.77 −  0.08/2 = 0.04 grams

Water Release Test

Immediately after the conclusion of the above Water Uptake Test the sample 2 as prepared above was subjected to the water release test. The sample was blotted to remove access water, weighted and the data were recorded. The sample was first exposed to ambient temperature for one half hour and weighed. Half an hour after weighing the sample, it was placed in a prewarmed (53° C.) test oven (small electrically heated oven, Quieny Lab Inc., Model 20 Lab oven or equivalent). The sample was left in the prewarmed oven for more than one hour and weighted. Thereafter the sample was placed back in the test oven and remained there for 3.5 hours.

From table VI it can be concluded that the water absorbed by sample 2 was released within 30 minutes exposure to ambient room temperature and humidity (48%). In fact, the sample registered a weight loss of 0.01 grams from its original weight which could seem to indicate that the label was not thoroughly dried at installation. So a preferred, label of 85.8 cm² size and 12.7 micron thickness has water release greater than 0 and less than 0.10 g/24 hours with a mean release of 0.045 g within 30 minutes given these parameters.

TABLE VI Water Release Test Sample 2 Room Oven Weight in Temperature Relative Temperature Time Grams (° F.) Humidity (° C.) 12:00 p.m. 59.85 g 72.6 48 53.5 12:30 p.m. 59.76 g 72.6 48 53.7  1:30 p.m. 59.76 g 52.3 Next 59.76 g 53.0 Reading  5:00 a.m.

Water Vapour Transmission Rate Test

The optimum combination of durability and washability of the labels according to the invention is at least partly due to the permeability of the label for the soaking solution. A sample of the transfer layer of the same type as tested in the water uptake/release test of a thickness of 12.7 microns was tested for water vapour transmission. A 25 milliliter glass container with a 15.9 millimeter diameter circular orifice was cleaned with acetone and filled with approximately 10 milliliters of deionized water. The orifice area of the container was heated to approximately 118° F. and a circle segment of the transfer layer was firmly applied using a small piece of silicone rubber as a pressure pad. After the container/label had cooled, the backing film was gently removed. The sample preparation was completed by adding a wax coating (0.001 g across the 1.99 cm² surface) and let air dry. A second glass container of the same dimensions as described above was cleaned thoroughly with acetone and filled with 10 milliliter of deionized water. The orifice area of the sample was heated as well. This sample was used as the control sample. The completed samples were then weighted various intervals over a 26.6 hour time period. The water vapour transmission rate over the total time of the experiment equated to 568.75 g/m² in a 24 hour time period at 22.2° C. at 46% relative humidity. It was found that a “steady state” water vapour transmission rate was not achieved until approximately 28 minutes from time 0. When using the “steady state” data after 28 minutes from time 0, the water vapour transmission rate was found to be about 526.93 g/m² in 24 hours.

For the control sample without a label, a water vapour transmission rate over the total time of the experiment of 1085.7 g/m² in 24 hours was found. The water vapour transmission rate of the preferred label according to the present invention will lie between 50 g/m² and 750 g/m² after 24 hours (22.2° C., 44% relative humidity), preferably around 500 g/m² after 24 hours. 

What is claimed is:
 1. Transfer label for application to a container, said transfer label comprising a backing layer and a transfer layer which is releasably attached to the backing layer, the transfer layer comprising an ink layer, wherein the transfer layer comprises on each side of the ink layer a top and a bottom containment layer respectively, the top and the bottom containment layers contacting one another outside a perimeter of the ink layer to form a closed envelope around the ink layer.
 2. Transfer label according to claim 1, wherein the ink layer comprises separate zones of dimensions between 0.5 mm² and 500 cm², the top containment layer and the bottom containment layer contacting one another outside the separate zones to form individual envelopes around each zone of the ink layer.
 3. Transfer label according to claim 2, wherein the majority of the envelopes enclosing the separate zones of the ink layer remain closed upon application of said transfer label to said container, said transfer layer being removable from said container via a wash process by contact with a washing liquid.
 4. Transfer label according to claim 3, wherein the transfer layer in the wash process breaks up in at least 4 pieces under soaking conditions in a turbulent aqueous liquid of a temperature below 100° C., within a soaking time of not more than 20 minutes, and is detached from the container, wherein a size of the majority of the pieces formed upon breaking up of the transfer layer is not smaller than the separate zones of the ink layer.
 5. A transfer label according to claim 4, wherein said aqueous liquid is below 70° C. and said soaking time is not more than 10 seconds.
 6. Transfer label according to claim 3 wherein the transfer layer outside the separate zones of the ink layer is permeable for the washing liquid.
 7. Transfer label according to claim 3, wherein the washing liquid is an aqueous alkaline solution.
 8. Transfer label according to claim 1, wherein the ink is water-soluble.
 9. Transfer label according to claim 1 wherein the top containment layer comprises an unpigmented ink, the bottom containment layer comprising an adhesive.
 10. Transfer label according to claim 1 wherein the top containment layer is discontinuous, and placed in register with the ink layer.
 11. Transfer label according to claim 1 wherein the bottom containment layer is discontinuous.
 12. Transfer label according to claim 1, wherein the transfer layer comprises a layer of adhesive having tack, said tack being at least reduced by contact with a soaking liquid.
 13. Transfer label according to claim 12, wherein the adhesive layer is discontinuous and is located in register with the ink layer.
 14. A transfer label according to claim 12, wherein said adhesive is dissolvable in said soaking liquid.
 15. A transfer label according to claim 12, wherein said adhesive is dissolvable in a washing liquid.
 16. Transfer label according to claim 1 with a thickness below 30 micrometers, and a weight of the containment layers between 1 g/m² and 10 g/m.
 17. A transfer label according to claim 16, wherein said thickness of said transfer label is less than 20 micrometers.
 18. Transfer label according to claim 1, comprising an adhesive layer of a weight between 1 and 10 g/m².
 19. A transfer label according to claim 18, wherein said adhesive layer is of a weight between 3 and 7 g/m².
 20. Transfer label according to claim 1, wherein the transfer layer comprises a layer of adhesive and wherein the adhesive layer comprises at least two sublayers, each of said sublayers having a respective tack, the tack of the sublayer which upon attaching to a container is closest to the container having a smaller tack than the layer of adhesive located further from the container.
 21. Container comprising a transfer layer which has been applied using a transfer label, said transfer label comprising a backing layer and the transfer layer which is releasably attached to the backing layer, the transfer layer comprising an ink layer and top and bottom containment layers respectively on each side of the ink layer, the top and the bottom containment layers contacting one another outside a perimeter of the ink layer to form a closed envelope around the ink layer.
 22. Container according to claim 21, said container further comprising a cover layer over the transfer layer, said cover layer comprising an acrylic wax.
 23. Container according to claim 21, wherein the transfer layer has been heat-treated via a method comprising the step of exposing said transfer layer on said container to a temperature between 40° C. and 100° C.
 24. A container according to claim 23, wherein said temperature is between 50° C. and 90° C.
 25. Container according to claim 21, comprising an application surface for receiving the transfer layer which application surface has a surface tension of at least 60 Dyne per cm.
 26. Container according to claim 21, wherein the label on the container has a pencil hardness between 1N and 7N in its dry state and a pencil hardness less than 0.5N after a soaking time between 1 and 15 minutes in water as a soaking solution at 20° C.
 27. Container according to claim 21, wherein the label on the container has a water uptake value after 3 hours greater than 0 and below 100 g/m².
 28. A container according to claim 27, wherein said water uptake value after 3 hours is about 5 g/m².
 29. Method of washing a container, said container comprising a transfer layer which has been applied using a transfer label, said transfer label comprising a backing layer and the transfer layer which is releasably attached to the backing layer, the transfer layer comprising an ink layer, wherein the transfer layer comprises on each side of the ink layer a top and a bottom containment layer respectively, the top and the bottom containment layers contacting one another outside a perimeter of the ink layer to form a closed envelope around the ink layer; said method comprising the steps of: a. placing the container in an aqueous soaking solution under turbulent conditions for a soaking time not longer than 20 minutes, said soaking solution having a temperature below 100° C., said label breaking up in at least 4 pieces, each piece not smaller than 5 micrometers and being detached from the container, whereby the majority of the ink remains contained inside the envelopes; b. pumping the soaking solution through a sieve and collecting the pieces of the label on the sieve; and c. periodically cleaning the sieve by collection and removal of the label pieces.
 30. Method according to claim 29, said sieve having openings having sizes, wherein the size of the openings of the sieve is between 0.1 mm and 10 mm.
 31. A method according to claim 30, wherein said size of said openings is about 2 mm.
 32. Method according to claim 29, further comprising the step of impingement of water jets on the container.
 33. Method according to claim 29, wherein the soaking solution comprises between 0.1 and 5% by weight, NaOH.
 34. A method according to claim 33, wherein said soaking solution comprises 0.5% NaOH.
 35. A method according to claim 29, wherein said soaking time is not longer than 1 minute, said temperature of said soaking solution is below 70° C., and said cleaning of said sieve by collection and removal of said label pieces occurs continuously. 